Photographic element having a transparent magnetic recording layer

ABSTRACT

A photographic element comprising a support having provided thereon a light-sensitive layer, a transparent magnetic recording layer, and a transparent reinforced filler layer coated over the transparent magnetic recording layer, the transparent magnetic recording layer comprising a transparent polymeric binder and ferro-magnetic particles, the magnetic particles having a surface area greater than 30 m 2  /gm and a coverage of from about 1×10 -11  mg/μm 3  to about 3×10 -10  mg/μm 3 , the transparent reinforced filler layer comprising a transparent polymeric binder and filler particles, the filler particles having a median diameter of less than 0.15 μm, a Mobs hardness of at least 6 and being present in an amount of from about 20 to about 300 percent by weight based on the weight of the polymeric binder.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to photographic elements and more particularly to photographic elements having a light-sensitive silver halide layer and a transparent magnetic recording layer.

2. Description of Related Art

It is known from various U.S. patents, including: U.S. Pat. Nos. 3,782,947; 4,279,945; 4,990,276; 5,217,804; 5,147,768; 5,229,259, and others; to include in a light-sensitive silver halide photographic element a transparent magnetic recording layer. Such elements are advantageous because they can be employed to record images by the customary photographic process while at the same time information can be recorded into and read from the magnetic recording layer by the techniques similar to that employed in the magnetic recording art.

A difficulty, however, arises in that magnetic recording layers generally employed in the magnetic recording industry are opaque, not only because of the nature of the magnetic particles, but also because of the requirements that the recording layer contains other additives which further create problems with regard to the optical characteristics of the layer. Also, the requirements of recording and reading of the magnetic signal from a transparent magnetic layer present on a photographic element are more stringent than that found in conventional magnetic recording because of the loading of the magnetic particles in the transparent magnetic layer and the nature of the photographic element.

Thus, the presence of the magnetic recording layer cannot interfere with the primary function of the photographic element which is to achieve realistic reproductions of the original image. In addition, the magnetic recording layer must be capable of accurately recording the information applied thereto and reading out the information on demand. This is particularly difficult because the loading and distribution of the magnetic particles in the transparent layer must be such as to not interfere with the quality of the photographic elements.

The photographic element and particularly the transparent magnetic recording layer provided thereon must be capable of repeated use in both the recording and reading mode and, therefore, must be durable, abrasion resistant and scratch resistant so as not to adversely affect the quality of the photographic element. For example, during the residence of the film in a camera, entries may be made to the magnetic recording layer for every exposure, and an indeterminate number of read operations are conducted depending on the particular application to which the film is used. This also is true in the processing of the film and in subsequent use of the processed film for additional copies, enlargements and the like.

Finally, after exposure of the photographic element, the film must pass through photofinishing equipment to allow developing and printing of the exposed film. Photofinishing equipment generally used in the photographic industry often contains film tracks or film guides through which the film must pass. These tracks or guides are usually fabricated from aluminum which could be subject to wear by particles contained in the film. Particulate generated by wear of the aluminum components could have a deleterious effect on images obtained during printing. Such wear could occur both from the surface of the film or from the edge of the film.

It can, therefore, be readily seen that it would be highly desirable to provide photographic elements having a transparent magnetic recording layer(s) which exhibits improved magnetic and photographic performance, improved running durability and scratch resistance. The extent to which the element abrades materials it contacts should be minimized without impacting the optical properties of the photographic element. This goal is extremely difficult to achieve because of the nature and concentration of the magnetic particles required to provide sufficient signal to write and read magnetically stored data, the effect of any noticeable color, haze, or grain associated with the magnetic layer on the photographic layers and the effect of the magnetic layer on the optical density and granularity of the photographic layers. Thus, all of these various characteristics must be considered both independently and cumulatively in order to arrive at a commercially viable photographic element containing a transparent magnetic recording layer that will withstand repeated and numerous passages through the recording and reading zones of a suitable apparatus. Also, because of the curl of the element, primarily due to the photographic layers and core set, the film must be held tightly against the magnetic heads by pressures much higher than those in conventional magnetic recording in order to maintain film plane flatness in the recording and reading zone.

SUMMARY OF THE INVENTION

The invention provides an improved photographic element including a support, having provided thereon a light-sensitive layer, a transparent magnetic recording layer, and a transparent reinforced filler layer coated over the transparent magnetic recording layer, the transparent magnetic recording layer comprising a transparent polymeric binder and ferro-magnetic particles, the magnetic particles having a surface area greater than 30 m² /gm and a coverage of from about 1×10⁻¹¹ mg/μm³ to about 3×10⁻¹⁰ mg/μm³, (1 μm=10⁻⁶ m) the transparent reinforced filler layer comprising a transparent polymeric binder and reinforcing filler particles, the reinforcing filler particles having a median diameter on a weight basis of less than 0.15 μm, a Mohs hardness of at least 6 and being present in the second layer in an amount of 20 to 300 percent based on the weight of the polymeric binder present. The transparent reinforced filler layer has a thickness of from about 0.2 to 0.8 μm. Optionally, the transparent reinforced filler layer may also be a magnetic recording layer containing similar ferromagnetic particles such that the total coverage of magnetic particles in both layers together is in the range stated above. Optionally, at least one of the layers may be crosslinked.

Because of the requirement that the magnetic layer be transparent in the photographic sense, it was highly unexpected to find that the addition of a further layer containing particulate material in the form of the reinforcing filler particles could be achieved without interfering with the optical and photographic properties of the element while at the same time achieving substantial increase in running durability of the element. In addition, the quite unexpected result of improved scratch resistance of a two layer structure was obtained.

DETAILED DESCRIPTION OF THE INVENTION

In the preparation of a photographic element having a transparent magnetic recording layer, the magnetic particles have a surface area greater than 30 m² /gm and preferably greater than 40 m² /gm. The coverage of the magnetic particles in the magnetic recording layer varies within the ranges given above depending upon the thickness of the magnetic recording layer. For optimum performance, the magnetic recording layer should be such that normal wear will not result in signal loss after multiple reading and writing operations. However, the layer must not be so thick as to interfere with the photographic properties of the film.

In accordance with this invention, the reinforcing filler particles have a median diameter of from 0.04 to 0.15 μm, preferably from 0.04 to 0.1 μm and most preferably from 0.04 to 0.08 μm. As a practical matter, the minimum median diameter is 0.04 μm. The reinforcing filler particles have a Mohs hardness greater than 6 and are present in the transparent reinforced filler layer in an amount of from about 20 percent to about 300 percent by weight and preferably 50 to 120 percent and most preferably from 65 to 85 percent based on the weight of the binder present. It was quite unexpected that such high quantities of additional particulate material could be present without affecting the transparency thereof in a photographic sense and at the same time increase the durability of the layer when running under high pressure against various surfaces.

When the magnetic particles are present in the transparent reinforced filler layer, they are present in an amount of from about 2 to about 12 percent by weight based upon the weight of the binder and most preferably in an amount of 5 to 10 percent. When present only in the magnetic recording layer, the magnetic particles are present in an amount of from about 1×10⁻¹¹ to about 3×10⁻¹⁰ mg/μm³.

In accordance with this invention, the transparent magnetic layer is prepared by initially forming a high solids content magnetic concentrate by mixing the magnetic particles in a suitable grind solvent together with suitable surfactants and milling in a device such as, for example, a ball mill, a roll mill, a high speed impeller mill, media mill, an attritor or a sand mill. Milling proceeds for a sufficient time to ensure that substantially no agglomerates of the magnetic particles remain. The high solids magnetic concentrate is next diluted with suitable solvents and polymeric stabilizers to maintain the particles in an unagglomerated state (subsequently referred to as the intermediate letdown). Mixing for an additional period of time is continued in order to polish the ingredients.

In a separate container, the binder polymer is dissolved in a suitable solvent. To this solution is added the intermediate letdown in accordance with the procedure set forth above and stirring is continued. This dispersion may be coated onto a suitable support in its present form or additional and optional ingredients such as, crosslinking agents, catalysts, coating aids, lubricants and the like, may be added before the coating operation. The transparent reinforced filler layer is coated to a dry thickness of from about 0.2 to about 0.8 μm.

The coating composition is applied to a suitable support which may contain additional layers for promoting adhesion, by any suitable coating device including slot die hoppers, slide hoppers, gravure coaters, reverse roll coaters and the like.

The transparent filler layer is prepared by initially forming a high solids content filler concentrate by mixing the filler particles in a suitable solvent together with suitable dispersants and milling a device as indicated above with respect to the magnetic particles. Milling proceeds for a sufficient time so there are no agglomerates of the filler particles and the high solids filler concentrate is diluted with suitable solvents and added to a binder solution. The filler coating solution is then coated, utilizing any of the above-mentioned coating devices, onto the already formed magnetic layer.

In an alternate embodiment, the magnetic layer and the filler layer are simultaneously cast using a slide hopper.

When a portion of the magnetic particles are incorporated into the filler layer in accordance with the above, the diluted filler coating composition is added to a portion of the intermediate letdown and coated in accordance with either of the embodiments set forth.

The transparent reinforced filler layer can also be overcoated with conventional layers including antistats, protective overcoats, lubricants and the like. In addition, the transparent reinforced filler layer may include materials which act as antistats or lubricants, or which allow the reinforced filler layer to act as a protective overcoat for the magnetic recording layer.

Any suitable support may be employed in the practice of this invention, such as, cellulose derivatives including cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetatepropionate and the like; polyamides; polycarbonates; polyesters, particularly polyethylene terephthalate, poly-1,4-cyclohexanedimethylene terephthalate, polyethylene 1,2-diphenoxyethane-4,4'-dicarboxylate, polybutylene terephthalate and polyethylene naphthalate; polystyrene, polypropylene, polyethylene, polymethyl-pentene, polysulfone, polyethersulfone, polyarylates, polyether imides and the like. Particularly preferred supports are polyethylene terephthalate, polyethylene naphthalate and the cellulose esters particularly cellulose triacetate.

Thickness of those supports used in the present invention is from 50 μm to 180 μm, preferably, 75 to 125 microns. In addition, various dyes may be formulated into the support or the magnetic layer to give neutral density.

Depending upon the nature of the support, suitable transparent tie or undercoat layers may be desired. Particularly with regard to polyester supports, primers are used in order to promote adhesion. Any suitable primers in accordance with those described in the following U.S. patents may be employed: U.S. Pat. Nos. 2,627,088; 3,501,301; 4,689,359; 4,363,872; and 4,098,952. Each of these are incorporated herein by reference in their entirety.

The ferromagnetic pigments comprise ferromagnetic iron oxides, such as γ-Fe₂ O₃, Fe₃ O₄ or γ-Fe₂ O₃ or Fe₃ O₄ with Co, Zn or other metals in solid solution or surface treated, or ferromagnetic chromium dioxides, such as CrO₂ or CrO₂ with metallic elements, for example Li, Na, Sn, Pb, Fe, Co, Ni and Zn, or halogen atoms in solid solution. Ferromagnetic metal pigments with an oxide coating on their surface to improve their chemical stability or to improve dispersibility, as is commonly used in conventional magnetic recording, may also be used in accordance with the invention. In addition, magnetic oxides with a thicker layer of lower refractive index oxide or other material having a lower optical scattering cross-section as taught in U.S. Pat. Nos. 5,217,804 and 5,252,444 may also be used. Cobalt surface treated iron oxide is the preferred ferromagnetic material for use in accordance with this invention.

The binders used in the magnetic layer and filler layer can be the same or different and include, for example, vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinyl acetate-vinyl alcohol copolymers, vinyl chloride-vinyl acetate-maleic acid polymers, vinyl chloride-vinylidene chloride copolymers, vinyl chloride-acrylonitrile copolymers, acrylic ester-acrylonitrile copolymers, acrylic ester-vinylidene chloride copolymers, methacrylic ester-vinylidene chloride copolymers, methacrylic ester-styrene copolymers, thermoplastic polyurethane resins, phenoxy resins, polyvinyl fluoride, vinylidene, chloride-acrylonitrile copolymers, butadiene-acrylonitrile copolymers, acrylonitrile-butadiene-acrylic acid copolymers, acrylonitrile-butadiene-methacrylic acid copolymers, polyvinyl butyral, polyvinyl acetal, cellulose derivatives, styrene-butadiene copolymers, polyester resins, phenolic resins, epoxy resins, thermosetting polyurethane resins, urea resins, melamine resins, alkyl resins, urea-formaldehyde resins and the like. Of the above, the cellulose derivatives are the preferred binders for use in accordance with this invention. Cellulose derivatives include cellulose esters such as, for example, cellulose acetate, cellulose diacetate, cellulose triacetate, cellulose acetate butyrate, cellulose acetate propionate, and the like. The most preferred binder for each layer is cellulose diacetate. For crosslinking of the binder with isocyanates, the binder should contain active hydrogen atoms as determined by the Zerewitinoff test, such active hydrogen atoms including --OH, --NH₂ --NHR, where R is an organic radical, and the like, as described in U.S. Pat. No. 3,479,310.

Dispersing agents, sometimes referred to as a wetting agent or a surface active agent, can be present in the dispersion to facilitate dispersion of the particles and/or wetting of the particles with the dispersing medium. This helps to further minimize agglomeration of the particles. Useful dispersing agents include fatty acid amines, and commercially available wetting agents such as Witco Emcol CC59 which is a quaternary amine available from Witco Chemical Corp. Rhodafac PE 510, Rhodafac RE 610, Rhodafac RE 960, and Rhodafac LO 529 which are phosphoric acid esters available from Rhone-Poulenc, and Solsperse 24000 which is a polyester-polyamine sold by Zeneca Inc. Other constituents of the coating composition, such as, grind solvents, coating aids, and solvents for the binder are included. Suitable grind solvents include, for example, organic acid esters such as phthalic acid esters. Preferred esters are dialkylesters of phthalic acid, the alkyl portion of which can contain from 1 to about 12, preferably 4 to 8, carbon atoms. Exemplary useful esters include dimethyl phthalate, diethyl phthalate, dioctyl phthalate, dipropyl phthalate, and dibutyl phthalate as disclosed in U.S. Pat. No. 4,990,276 issued to Bishop et al. and assigned to the same assignee as this application.

Suitable coating aids include nonionic fluorinated alkyl esters such as, FC-430, FC-431 sold by Minnesota Mining and Manufacturing Co., polysiloxanes such as, Dow Corning DC 1248, DC 200, DC 510, DC 190 sold by Dow Corning and BYK 310, BYK 320, and BYK 322 sold by BYK Chemie and SF 1079, SF 1023, SF 1054 and SF 1080 sold by General Electric.

Organic solvents are normally used for the preparation of the dispersion. Examples of suitable solvents are ketones, such as acetone, methyl ethyl ketone and cyclohexanone; alcohols, including methanol, ethanol, and the like; esters, such as ethyl acetate and butyl acetate; cellosolves; ethers, such as tetrahydrofuran; aromatic solvents, such as toluene; and chlorinated hydrocarbons, such as carbon tetrachloride, chloroform, dichloromethane; tetrahydrofuran and the ketoesters of U.S. application Ser. No. 08/173,833 filed Dec. 22, 1993, entitled Coating Compositions For A Transparent Magnetic Recording Layer, by R. M. Wexler and assigned to the same assignee as the immediate application. Mixtures of chlorinated hydrocarbons, ketones, and ketoesters are preferred.

Optionally, the binder in the magnetic layer may be crosslinked employing any suitable crosslinking agent such as, for example, organic isocyanates; aziridines, as taught in U.S. Pat. No. 4,225,665; and melamines such as methoxymethylmelamine, and the like as set forth in U.S. Pat. No. 5,198,499 to Anderson et al. issued Mar. 30, 1993 and assigned to the same assignee as this application.

Any suitable organic polyisocyanate can be used as the crosslinking agent such as, tetramethylene diisocyanate, hexamethylene diisocyanate, diisocyanato dimethylcyclohexane, dicyclohexylmethane diisocyanate, isophorone diisocyanate, dimethylbenzene diisocyanate, methylcyclohexylene diisocyanate, lysine diisocyanate, tolylene diisocyanate, diphenylmethane diisocyanate, polymers of the foregoing, polyisocyanates prepared by reacting an excess of an organic diisocyanate with an active hydrogen containing compounds such as polyols, polyethers and polyesters and the like including ethylene glycol, propylene glycol, dipropylene glycol, butylene glycol, trimethylol propane, hexanetriol, glycerine, sorbitol, pentaerythritol, caster oil, ethylenediamine, hexamethylenediamine, ethanolamine, diethanolamine, triethanolamine, water, ammonia, urea and the like, including biuret compounds, allophanate compounds and the like. The preferred polyisocyanates employed as a crosslinking agent is the reaction product of trimethylol propane and 2,4-tolylene diisocyanate sold by Mobay under the trade designation Mondur CB 75.

Examples of the reinforcing filler particles include nonmagnetic inorganic powders with a Mohs scale hardness of at least 6. Specific examples are metal oxides such as γ-aluminum oxide, chromium oxide (Cr₂ O₃), iron oxide (alpha-Fe₂ O₃), tin oxide, doped tin oxide, such as antimony or indium doped tin oxide, silicon dioxide, alumino-silicate and titanium dioxide; carbides such as silicon carbide and titanium carbide; and diamond in fine powder. Gamma aluminum oxide and silicon dioxide are preferred. The important feature is that the filler particles have the particle size and are used in the amounts expressed above.

As noted, photographic elements in accordance with this invention comprise at least one photosensitive layer. Such photosensitive layers can be image-forming layers containing photographic silver halides such as silver chloride, silver bromide, silver bromoiodide, silver chlorobromide and the like. Both negative and reversal silver halide elements are contemplated. For reversal films, the emulsion layers as taught in U.S. Pat. No. 5,236,817, especially Examples 16 and 21, are particularly suitable. Any of the known silver halide emulsion layers, such as those described in Research Disclosure, Vol. 176, December 1978 Item 17643 and Research Disclosure Vol. 225, January 1983 Item 22534, the disclosures of which are incorporated by reference in their entirety, are useful in preparing photographic elements in accordance with this invention. Generally, the photographic element is prepared by coating the support film on the side opposite the magnetic recording layer with one or more layers comprising a dispersion of silver halide crystals in an aqueous solution of gelatin and optionally one or more subbing layers, such as, for example, gelatin, etc. The coating process can be carried out on a continuously operating machine wherein a single layer or a plurality of layers are applied to the support. For multicolor elements, layers can be coated simultaneously on the composite support film as described in U.S. Pat. Nos. 2,761,791 and 3,508,947. Additional useful coating and drying procedures are described in Research Disclosure, Vol. 176, December 1978, Item 17643. Suitable photosensitive image forming layers are those which provide color or black and white images.

As is taught in U.S. Pat. No. 3,782,947 noted above, whether an element is useful for both photographic and magnetic recording depends on both the size distribution and concentration of the magnetic particles and on the relationship between the granularities of the magnetic and photographic coatings. Generally, of course, the coarser the grain of the emulsion in the photographic element that contains the magnetic recording layer, the larger the mean size of the magnetic particles which can be tolerated. A magnetic particle concentration between about 10 and 1000 mg/m² when uniformly distributed across the desired area of the photographic element will be sufficiently photographically transparent provided that the maximum particle size is less than about 1 micron. Particle concentrations less than about 10 mg/m² tend to be insufficient for magnetic recording purposes and particle concentrations greater than about 1000 mg/m² tend to be too dense for photographic purposes. Particularly useful particle concentrations are in the range of 20-70 mg/m². Concentrations of about 30 mg/m² have been found to be particularly useful in reversal films and concentrations of about 60 mg/m² are particularly useful in negative films.

The photographic elements according to this invention can contain one or more conducting layers such as antistatic layers and/or anti-halation layers such as such as described in Research Disclosure, Vol. 176, December 1978, Item 17643 to prevent undesirable static discharges during manufacture, exposure and processing of the photographic element. Antistatic layers conventionally used in color films have been found to be satisfactory for use herewith. Any of the antistatic agents set forth in U.S. Pat. No. 5,147,768, which is incorporated herein by reference may be employed. Preferred antistats include metal oxides, for example, tin oxide, antimony doped tin oxide and vanadium pentoxide.

The photographic elements according to this invention can be provided with a protective or lubricating layer, such as a wax layer, in or over the transparent magnetic recording layer. Suitable lubricants include silicone oil, silicones having polar groups, fatty acid-modified silicones, fluorine-containing silicones, fluorine-containing alcohols, fluorine-containing esters, polyolefins, polyglycols alkyl phosphates and alkali metal salts thereof, alkyl sulfates and alkali metal salts thereof, polyphenyl ethers, fluorine-containing alkyl sulfates and alkali metal salts thereof, monobasic fatty acids having 10 to 24 carbon atoms (which may contain unsaturated bonds or may be branched) and metal salts thereof (such as Li, Na, K and Cu), monovalent, divalent, trivalent, tetravalent, pentavalent and hexavalent alcohols having 12 to 22 carbon atoms (which may contain unsaturated bonds or may be branched), alkoxy alcohols having 12 to 22 carbon atoms, mono-, di- and tri-esters of monobasic fatty acids having 10 to 24 carbon atoms (which may contain unsaturated bonds or may be branched) and one of monovalent, divalent, trivalent, tetravalent, pentavalent and hexavalent alcohols having 2 to 12 carbon atoms (which may contain unsaturated bonds or may be branched), fatty acid esters of monoalkyl ethers of alkylene oxide polymers, fatty acid amides having 8 to 22 carbon atoms and aliphatic amines having 8 to 22 carbon atoms.

Specific examples of these compounds (i.e., alcohols, acids or esters) include lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, butyl stearate, oleic acid, linolic acid, linolenic acid, elaidic acid, octyl stearate, amyl stearate, isooctyl stearate, butyl myristate, octyl myristate, butoxyethyl stearate, anhydrosorbitan monostearate, anhydrosorbitan distearate, anhydrosorbitan tristearate, pentaerythrityl tetrastearate, oleyl alcohol and lauryl alcohol. Carnauba wax is preferred.

The invention will be further illustrated by the following examples in which parts and percentages are given by weight unless otherwise specified.

EXAMPLE 1

A cellulose diacetate/cellulose triacetate binder with magnetic particles is cast to a dry thickness of about 0.8 microns onto subbed polyethylene terephthalate support and overcoated with a cellulose diacetate binder with reinforcing filler particles cast to a dry thickness of about 0.45 microns from a dispersion compositions as shown in Table 1. The dispersions are prepared by adding the respective particle dispersions with respective stabilizing agents and solvents to a cellulose diacetate solution in methylene chloride/acetone/methyl acetoacetate using a high shear mixer. A coating aid is then added with low shear. Subsequently, the cast layers are overcoated with 2.5 mg/sq.ft. of carnauba wax.

                                      TABLE 1                                      __________________________________________________________________________     Dispersion Ingredient Function      Percent                                    __________________________________________________________________________     Transparent Magnetic Recording Layer                                           Cellulose Diacetate   Binder        1.87                                       Cellulose Triacetate  Binder/Dispersion Stabilizer                                                                 0.083                                      Toda CSF-4085V2 (Toda Kogyo)                                                                         Magnetic Particle                                                                            0.083                                      Rhodafac PE510 (Rhone-Poulenc)                                                                       Surfactant    0.004                                      Dibutyl Phthalate     Grind Solvent 0.163                                      FC-431 (3M Co.)       Coating Aid   0.015                                      Methylene chloride    Solvent       68.447                                     Acetone               Solvent       24.446                                     Methyl acetoacetate   Solvent       4.889                                      Transparent Reinforcing Filler Layer                                           Cellulose Diacetate   Binder        1.025                                      Cellulose Triacetate  Binder/Dispersion Stabilizer                                                                 0.0765                                     Toda CSF-4085V2       Magnetic Particle                                                                            0.0765                                     Rhodafac PE510        Surfactant    0.004                                      Dibutyl Phthalate     Grind Solvent 0.153                                      Degussa Oxide C (0.04 μm median diameter)                                                         Reinforcing Filler Particle                                                                  1.130                                      Mobay Mondur CB75     Crosslinking Agent                                                                           0.154                                      Tin Octoate           Catalyst      0.008                                      Zeneca Solsperse 24000                                                                               Dispersant    0.226                                      FC-431                Coating Aid   0.015                                      Methylene chloride    Solvent       67.992                                     Acetone               Solvent       24.283                                     Methyl acetoacetate   Solvent       4.857                                      __________________________________________________________________________

Comparative Example C-1

A single layer is coated from the composition shown in Table 2 in which reinforcing filler particles are added to the cellulose diacetate/cellulose triacetate binder with magnetic particles. The layer is subsequently overcoated with 2.5 mg/sq.ft. of carnauba wax.

                                      TABLE 2                                      __________________________________________________________________________     Dispesrsion Ingredient                                                                               Function      Percent                                    __________________________________________________________________________     Transparent Magnetic Recording Layer                                           Cellulose Diacetate   Binder        1.5                                        Cellulose Triacetate  Binder/Dispersion Stabilizer                                                                 0.1295                                     Toda CSF-4085V2       Magnetic Particle                                                                            0.1295                                     Dibutyl Phthalate     Grind Solvent 0.267                                      Mobay Mondur CB-75    Crosslinking Agent                                                                           0.375                                      Tin Octoate           Catalyst      0.019                                      Rhodafac PE510        Surfactant    0.006                                      Degussa Oxide C (0.06 μm median diameter)                                                         Reinforcing Filler Particle                                                                  1.6                                        Zeneca Solsperse 24000                                                                               Dispersant    0.32                                       FC-431                Coating Aid   0.015                                      Methylene chloride    Solvent       66.947                                     Acetone               Solvent       23.910                                     Methyl acetoacetate   Solvent       4.782                                      __________________________________________________________________________

EVALUATION METHODS

Scratch Resistance

The resistance to scratches of lubricated cast layers is evaluated by a single arm scratch test. This test consists of determining the load in grams required to produce a visible scratch on a piece of film using a 0.076 mm (3 mils) sapphire sylus. The load to scratch is determined by the first visible scratch viewed against a fluorescent light and when projected with a slide projector and viewed at 4.57 m (15 feet).

                  TABLE 3                                                          ______________________________________                                                      First Visible Load to Scratch (grams)                             Sample         Transmission                                                                               4.57 m Projection                                   ______________________________________                                         Example 1      60          130                                                 Comparative Example C-1                                                                       40          110                                                 ______________________________________                                    

EXAMPLES 2

A color photographic recording material for color negative development is prepared by applying the following layers in the given sequence to the opposite side of each of the supports of Example 1 and Comparative Example 1 respectively. The quantities of silver halide are given in grams (g) of silver per m². The quantities of other materials are given in g per m².

Layer 1 {Antihalation Layer} black colloidal silver sol containing 0.236 g of silver, with 2.44 g gelatin.

Layer 2 {First (least) Red-Sensitive Layer} Red sensitized silver iodobromide emulsion [1.3 mol % iodide, average grain diameter 0.55 microns, average thickness 0.08 microns] at 0.49 g, red sensitized silver iodobromide emulsion [4 mol % iodide, average grain diameter 1.0 microns, average thickness 0.09 microns] at 0.48 g, cyan dye-forming image coupler C-1 at 0.56 g, cyan dye-forming masking coupler CM-1 at 0.033 g, BAR compound B-1 at 0.039 g, with gelatin at 1.83 g.

Layer 3 {Second (more) Red-Sensitive Layer} Red sensitive silver iodobromide emulsion [4 mol % iodide, average grain diameter 1.3 microns, average grain thickness 0.12 microns] at 0.72 g, cyan dye-forming image coupler C-1 at 0.23 g, cyan dye-forming masking coupler CM-1 at 0.022 g, DIR compound D-1 at 0.011 g, with gelatin at 1.66 g.

Layer 4 {Third (most) Red-Sensitive Layer} Red sensitized silver iodobromide emulsion [4 mol % iodide, average grain diameter 2.6 microns, average grain thickness 0.13 microns] at 1.11 g, cyan dye-forming image coupler C-1 at 0.13 g, cyan dye-forming masking coupler CM-1 at 0.033 g, DIR compound D-1 at 0.024 g, DIR compound D-2 at 0.050 g, with gelatin at 1.36 g.

Layer 5 {Interlayer} Yellow dye material YD-1 at 0.11 g and 1.33 g of gelatin

Layer 6 {First (least) Green-Sensitive Layer} Green sensitized silver iodobromide emulsion [1.3 mol % iodide, average grain diameter 0.55 microns, average grain thickness 0.08 microns] at 0.62 g, green sensitized silver iodobromide emulsion [4 mol % iodide, average grain diameter 1.0 microns, average grain thickness 0.09 microns] at 0.32 g, magenta dye-forming image coupler M-1 at 0.24 g, magenta dye-forming masking coupler MM-1 at 0.067 g with gelatin at 1.78 g.

Layer 7 {Second (more) Green-Sensitive Layer} Green sensitized silver iodobromide emulsion [4 mol % iodide, average grain diameter 1.25 microns, average grain thickness 0.12 microns] at 1.00 g, magenta dye-forming image coupler M-1 at 0.091 g, magenta dye-forming masking coupler MM-1 at 0,067 g, DIR compound D-1 at 0.024 g with gelatin at 1.48 g.

Layer 8 {Third (most) Green-Sensitive Layer) Green sensitized silver iodobromide emulsion [4 mol % iodide, average grain diameter 2.16 microns, average grain thickness 0.12 microns] at 1.00 g, magenta dye-forming image coupler M-1 at 0.0.72 g, magenta dye-forming masking coupler MM-1 at 0.056 g, DIR compound D-3 at 0.01 g, DIR compound D-4 at 0.011 g, with gelatin at 1.33 g.

Layer 9 {Interlayer} Yellow dye material YD-2 at 0.11 g with 1.33 g gelatin.

Layer 10 {First (less) Blue-Sensitive Layer} Blue sensitized silver iodobromide emulsion [1.3 mol % iodide, average grain diameter 0.55, average grain thickness 0.08 microns] at 0.24 g, blue sensitized silver iodobromide emulsion [6 mol % iodide, average grain diameter 1.0 microns, average grain thickness 0.26 microns] at 0.61 g, yellow dye-forming image coupler Y-1 at 0.29 g, yellow dye forming image coupler Y-2 at 0.72 g, cyan dye-forming image coupler C-1 at 0.017 g, DIR compound D-5 at 0.067 g, BAR compound B-1 at 0.003 g with gelatin at 2.6 g.

Layer 11 {Second (more) Blue-Sensitive Layer} Blue sensitized silver iodobromide emulsion [4 mol % iodide, average grain diameter 3.0 microns, average grain thickness 0.14 microns] at 0.23 g, blue sensitized silver iodobromide emulsion [9 mol % iodide, average grain diameter 1.0 microns] at 0.59 g, yellow dye-forming image coupler Y-1 at 0.090 g yellow dye-forming image coupler Y-2 at 0.23 g, cyan dye-forming image coupler C-1 0.022 g, DIR compound D-5 at 0.05 g, BAR compound B-1 at 0.006 g with gelatin at 1.97 g.

Layer 12 {Protective Layer} 0.111 g of dye UV-1, 0.111 g of dye UV-2, unsensitized silver bromide Lippman emulsion at 0.222 g, 2.03 g.

This film is hardened at coating with 2% by weight to total gelatin of hardener H-1. Surfactants, coating aids, scavengers, soluble absorber dyes and stabilizers are added to the various layers of this sample as is commonly practiced in the art.

The formulas for the component materials are as follows: ##STR1##

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention. 

What is claimed is:
 1. A photographic element comprising a support having provided thereon a light-sensitive layer, a transparent magnetic recording layer, and a transparent reinforced filler layer coated over the transparent magnetic recording layer, the transparent magnetic recording layer comprising a transparent polymeric binder and ferro-magnetic particles, the magnetic particles having a surface area greater than 30 m² /gm and a coverage of from about 1×10⁻¹¹ mg/μm³ to about 3×10⁻¹⁰ mg/m³, the transparent reinforced filler layer comprising a transparent polymeric binder and filler particles, the filler particles having a median diameter of less than 0.15 μm, a Mohs hardness of at least 6 and being present in an amount of from about 20 to about 300 percent by weight based on the weight of the polymeric binder.
 2. The photographic element of claim 1 wherein the filler particles are present in an amount of from 50 to 120 percent.
 3. The photographic element of claim 1 wherein the filler particles are present in an amount of from 65 to 85 percent.
 4. The photographic element of claim 1 wherein the filler particles have a median diameter of from 0.04 to 0.15 μm.
 5. The photographic element of claim 1 wherein the filler particles have a median diameter of from 0.04 to 0.1 μm.
 6. The photographic element of claim 1 wherein the filler particles have a median diameter of from 0.04 to 0.08 μm.
 7. The photographic element of claim 1 wherein the reinforcing filler particles are gamma aluminum oxide.
 8. The photographic element of claim 1 wherein the thickness of the transparent reinforced filler layer is from about 0.2 μm to about 0.8 μm.
 9. The photographic element of claim 1 wherein ferromagnetic particles are also present in transparent reinforced filler layer and the total coverage of ferromagnetic particles in both layers is from about 1×10⁻¹¹ mg/μm³ to about 1×10⁻¹⁰ mg/μm³.
 10. The photographic element of claim 9 where the ferromagnetic particles are present in the reinforcing filler layer in an amount of from about 2 to about 12 percent by weight based on the weight of the polymeric binder present in the reinforcing filler layer.
 11. The photographic element of claim 10 wherein the ferromagnetic particles are present in the amount of from about 5 to 10 percent by weight.
 12. The photographic element of claim 1 wherein a polymeric binder is a cellulose ester, a polyurethane or a vinyl polymer.
 13. The photographic element of claim 1 wherein a polymeric binder is crossed-linked. 